Product Description:
HAYNES® 230-W® coated electrodes are used for the shielded metal arc welding of HAYNES® 230®. The deposited weld metal has excellent high-temperature strength and outstanding resistance to oxidizing environments up to 2100°F for prolonged exposures. The deposited weld metal also has excellent long-term stability.
Specifications:
AWS A 5.11 ENiCrWMo-1 UNS W86231
Composition:
| Nickel | Remainder |
| Chromium | 20.00-24.00 |
| Tungsten | 13.00-15.00 |
| Cobalt | 5.00 max. |
| Iron | 3.00 |
| Molybdenum | 1.00-3.00 |
| Manganese | 0.30-1.00 |
| Silicon | 0.25-0.75 |
| Other | 0.50 max. |
| Copper | 0.50 max. |
| Aluminum | 0.50 max. |
| Titanium | 0.10 max. |
| Carbon | 0.10 max. |
| Phosphorus | 0.02 max. |
| Sulfur | 0.0015 |
Minimal Mechanical Properties:
| Tensile (psi) | 90,000 |
| Mpa | 620 |
| Elongation (%) | 20 |
Available Product Forms and Sizes:
| Diameter in | 0.093 | 0.125 | 0.156 | 0.187 |
| Diameter mm | 2.40 | 3.20 | 4.00 | 4.70 |
| Length in | 10 | 14 | 14 | 14 |
| Length mm | 254 | 355.6 | 355.6 | 355.6 |
| Package Weight lbs. | 5 | 10 | 10 | 10 |
| Current (A) DCEP | 40-70 | 70-100 | 80-140 | 120-150 |