HAYNES® 214® RTW™ Filler Metal (Structural)

Product Description:

HAYNES® 214® RTW filler metal is used for the gas metal arc and gas tungsten arc welding of HAYNES® 214® alloy. The deposited weld metal has outstanding oxidation resistance to 2300°F and excellent resistance to carburization and excellent resistance to chlorine-bearing environments. The alloy is used in demanding industrial heating applications and specialized gas turbine parts, such as honeycomb seals. The RTW finish on the spooled wire promotes smooth feeding through welding equipment and reduced tip wear in contact tips.

Specifications:

HAYNES PS-6076-2    UNS N07214

Composition:

Nickel: Balance
Chromium: 15.00-17.00
Aluminum: 4.10-5.00
Iron: 2.00-4.00
Cobalt: 2.00 max.
Manganese: 0.50 max.
Molybdenum: 0.50 max.

Titanium: 0.50 max.
Tungsten: 0.50 max.
Silicon: 0.20 max.
Niobium: 0.15 max.
Carbon: 0.05 max.
Yttrium: 0.003-0.04
Zirconium: 0.02 max.

Phosphorus: 0.015 max.
Sulfur: 0.015 max.
Magnesium: 0.010 max.
Boron 0.004 max.

Minimal Mechanical Properties:

Tensile (psi)
Mpa
Elongation (%)

Available Product Forms and Sizes:

Diameter in 0.030 0.031 0.035 0.039 0.045 0.047 0.062 0.078 0.093 *0.125 *0.156x 0.187x
Diameter mm 0.76 0.80 0.89 1.00 1.10 1.20 1.60 2.00 2.40 *3.20 *4.00x *4.70x

Filler metals are available in MIG spools, TIG cut lengths, reels, and coils from the above diameters.

*Size not available in MIG spools.

˟Size not available on reels.

Standard TIG straight lengths are available in 36” (914mm) lengths. Other lengths available upon request.