Tensile Data

Tensile properties after heat treating at
2050°F (1121°C) /30 min./RAC + 1650°F (899°C) /4h/AC

Test Temperature 0.2% Yield Strength Ultimate Tensile Strength 4D Elongation
°F °C ksi MPa ksi MPa %
RT RT 116.4 803 181.8 1253 20.5
400 204 109* 752* 174.2* 1201* 16.5*
800 427 109.1* 752* 161.6* 1114* 20.3*
1000 538 107.2 739 161 1110 21.2
1200 649 107.7 743 172.9 1192 19.3
1400 760 114.3 788 139.1 959 28.3
1500 816 104* 717* 115.7* 798* 27.2*
1600 871 79.7 550 89.2 615 28.5
1700 927 59.1* 407* 66.9* 461* 24.8*
1800 982 34.2 236 40.2 277 31.1
2000 1093 4.9* 34* 8.5* 59* 94.4*

*Limited data

Tensile properties after heat treating at 1400°F (760°C) /16h/AC

Test Temperature 0.2% Yield Strength Ultimate Tensile Strength 4D Elongation
°F °C ksi MPa ksi MPa %
RT RT 154.3 1064 205.4 1416 22.3
400 204 141.2* 974* 198.2* 1367* 23.0*
800 427 141.8* 978* 181.6* 1252* 25.6*
1000 538 139.8 964 182.6 1259 20.5
1200 649 138.3 954 196.2 1353 23.4
1400 760 126.1 869 150.8 1040 17.9
1500 816 112.2 774 128.1 883 19.4
1600 871 83.9 578 98.5 679 31.4
1700 927 51.1 352 62.3 430 38.7
1800 982 25.9 179 34.5 238 42.7

*Limited data