Condition |
0.2% Yield Strength |
Ultimate Tensile Strength |
4D Elongation |
Reduction of Area |
Impact Strength |
ksi |
MPa |
ksi |
MPa |
% |
% |
ft.-lbs. |
J |
Solution Annealed |
50.2 |
346 |
116.3 |
802 |
56.3 |
50.9 |
186.5* |
253* |
+ 1200°F (649°C)/ 1,000 hr. |
83.3 |
574 |
145.9 |
1006 |
37.6 |
40.0 |
53.5 |
73 |
+ 1200°F (649°C)/ 4,000 hr. |
88.5 |
610 |
152.4 |
1051 |
34.4 |
36.4 |
53.4 |
72 |
+ 1200°F (649°C)/ 8,000 hr. |
90.4 |
623 |
152.8 |
1054 |
34.3 |
36.6 |
51.5 |
70 |
+ 1400°F (760°C)/ 1,000 hr |
71.6 |
494 |
138.7 |
956 |
39.7 |
45.2 |
57.0 |
77 |
+ 1400°F (760°C)/ 4,000 hr |
67.9 |
468 |
136.5 |
941 |
38.6 |
41.2 |
51.3 |
70 |
+ 1400°F (760°C)/ 8,000 hr |
64.5 |
445 |
136.0 |
938 |
37.1 |
36.9 |
35.5 |
48 |
+ 1400°F (760°C)/ 1,000 hr. |
50.7 |
350 |
121.2 |
836 |
49.9 |
51.7 |
90.0 |
122 |
+ 1600°F (871°C)/ 4,000 hr. |
49.7 |
343 |
119.7 |
825 |
48.0 |
51.3 |
80.6 |
109 |
+ 1600°F (871°C)/ 8,000 hr. |
47.6 |
328 |
118.8 |
819 |
49.8 |
50.5 |
67.0 |
91 |