Oxidation Resistance

2100°F (1149°C) in Air for 1,008 h – Cycled Weekly


Alloy Metal Loss Avg. Metal Affected
mils/side (μm/side) mils/side (μm/side)
214® 0.1 (3) 0.5 (13)
233®
0.2 (5) 0.5 (13)
230® 1.2 (30) 4.4 (112)
617 1.0 (25) 5.2 (132)
X 3.6 (91) 6.1 (155)

*Average Metal Affected = Metal Loss + Internal Attack