Tensile Data
Form
|
Test Temperature
|
0.2% Offset
Yield Strength
|
Ultimate Tensile
Strength
|
Elongation
|
Sheet
0.045 to 0.063 in
(1.1 to 1.6 mm)
thick
|
°F
|
°C
|
ksi
|
MPa
|
ksi
|
MPa
|
%
|
RT |
RT |
64.5 |
444 |
129.8 |
844 |
49 |
1000 |
538 |
49.1 |
338 |
112.3 |
773 |
50 |
1200 |
649 |
46.7 |
322 |
104.5 |
720 |
56 |
1400 |
760 |
45.1 |
311 |
84.1 |
574 |
70 |
1600 |
871 |
31.6 |
218 |
48.6 |
341 |
47 |
1800 |
982 |
16.0 |
110 |
28.0 |
193 |
46 |
2000 |
1093 |
7.6 |
52 |
15.9 |
110 |
75 |
Plate
3/8 to 1-in
(9.5 to 25.4 mm)
thick
|
RTa |
RTa |
55.6 |
383 |
123.1 |
849 |
55 |
200 |
93 |
52.9 |
365 |
118.0 |
814 |
60 |
400 |
204 |
48.0 |
331 |
114.4 |
789 |
59 |
600 |
316 |
42.2 |
291 |
109.7 |
756 |
63 |
800 |
427 |
43.1 |
297 |
108.9 |
751 |
62 |
1000 |
538 |
41.0 |
283 |
105.9 |
727 |
61 |
1200 |
649 |
39.8 |
274 |
99.1 |
683 |
59 |
1400 |
760 |
39.3 |
271 |
79.3 |
547 |
69 |
1600 |
871 |
33.8 |
233 |
52.7 |
363 |
57 |
1800 |
982 |
19.6 |
135 |
33.0 |
228 |
62 |
2000 |
1093 |
8.8 |
61 |
17.0 |
117 |
69 |
a-Based pm 34 tests. At other temperatures, the number of tests varied from 7-23.
RT=Room Temperature
Average Aged Tensile Data, Room Temperature*
Form
|
Aging
Temperature
|
Aging Time
|
0.2% Offset
Yield Strength
|
Ultimate Tensile
Strength
|
Elongation
|
°F
|
°C
|
h
|
ksi |
MPa |
ksi
|
MPa
|
%
|
Sheet
0.057 in
(1.45 mm)
thick
|
Solution-annealed |
- |
128.6 |
887 |
63.0 |
434 |
58 |
1000 |
538 |
1000 |
178.6 |
1231 |
109.2 |
753 |
45 |
4000 |
181.7 |
1253 |
107.5 |
741 |
41 |
8000 |
185.1 |
1276 |
119.1 |
821 |
41 |
16000 |
186.8 |
1288 |
120.5 |
831 |
38 |
1200 |
649 |
1000 |
133.4 |
920 |
69.3 |
478 |
56 |
4000 |
130.3 |
898 |
66.3 |
457 |
52 |
8000 |
132.5 |
914 |
65.9 |
454 |
54 |
16000 |
133.1 |
918 |
68.4 |
472 |
50 |
1400 |
760 |
1000 |
133.3 |
919 |
66.6 |
459 |
54 |
4000 |
132.2 |
910 |
64.9 |
447 |
51 |
8000 |
131.1 |
904 |
65.3 |
450 |
54 |
16000 |
128.3 |
885 |
62.6 |
432 |
52 |
Plate
½ in
(12.7 mm)
thick
|
Solution Heat-Treated |
- |
125.3 |
864 |
52.9 |
365 |
54 |
800 |
427 |
1000 |
125.7 |
867 |
55.9 |
385 |
60 |
4000 |
126.9 |
875 |
55.5 |
383 |
60 |
8000 |
126.7 |
874 |
56.6 |
390 |
55 |
16000 |
128.0 |
883 |
57.9 |
399 |
56 |
1000 |
538 |
1000 |
144.4 |
996 |
71.5 |
493 |
46 |
4000 |
175.0 |
1207 |
102.5 |
707 |
44 |
8000 |
180.8 |
1247 |
108.2 |
746 |
38 |
16000 |
182.5 |
1258 |
108.9 |
751 |
39 |
1200 |
649 |
1000 |
125.1 |
863 |
56.6 |
390 |
57 |
4000 |
125.8 |
867 |
56.4 |
389 |
54 |
8000 |
127.2 |
877 |
57.0 |
393 |
50 |
16000 |
127.9 |
882 |
59.3 |
409 |
49 |
1400 |
760 |
1000 |
126.0 |
869 |
53.7 |
370 |
55 |
4000 |
127.4 |
878 |
54.1 |
373 |
52 |
8000 |
127.5 |
879 |
53.5 |
369 |
46 |
16000 |
127.5 |
879 |
53.9 |
372 |
47 |
1600 |
871 |
1000 |
125.8 |
867 |
50.8 |
350 |
58 |
4000 |
125.2 |
863 |
50.7 |
350 |
56 |
8000 |
123.5 |
852 |
51.3 |
354 |
53 |
16000 |
123.3 |
850 |
50.5 |
348 |
56 |
*Test Data for each form are from a single heat.
Average Welded and Aged Tensile Data, Room Temperature*
Form
|
Aging
Temperature
|
Aging Time
|
0.2% Offset
Yield Strength
|
Ultimate
Tensile Strength
|
Elongation
|
°F
|
°C
|
h
|
ksi
|
Mpa
|
ksi
|
MPa
|
%
|
Gas Tungsten arc
Welded Plate
½ in (12.7mm)
Thick
|
Solution-annealed |
- |
59.8 |
412 |
112.4 |
775 |
62 |
1000 |
63.3 |
436 |
121.7 |
839 |
33 |
4000 |
60.4 |
416 |
122.8 |
847 |
32 |
1200 |
649 |
8000 |
62.2 |
429 |
119.1 |
821 |
26 |
16000 |
63.6 |
439 |
155.6 |
1073 |
25 |
All Weld
Metal** |
Solution-annealed |
- |
66.6 |
459 |
105.1 |
725 |
55 |
1300** |
98.4 |
678 |
139.8 |
964 |
24 |
1000 |
538 |
4000** |
107.6 |
742 |
145.6 |
1004 |
26 |
1000 |
60.7 |
419 |
102.5 |
707 |
24 |
4000 |
52.9 |
365 |
110.3 |
760 |
25 |
1200 |
649 |
8000 |
61.7 |
425 |
102.3 |
705 |
20 |
16000 |
66.4 |
458 |
110.3 |
760 |
21 |
*Test data for each form are form a single heat
**Gas tungsten arc welded