Physical Properties

Physical Property British Units Metric Units
Density RT 0.305lb/in3 RT 8.44 g/cm3
Melting Range 2350-2460°F - 1288-1349°C -
Electrical Resistivity RT 50.8 µohm-in RT 129 µohm-cm
200°F 52.0 µohm-in 100°C 132 µohm-cm
400°F 52.8 µohm-in 200°C 134 µohm-cm
600°F 53.1 µohm-in 300°C 135 µohm-cm
800°F 53.5 µohm-in 400°C 136 µohm-cm
1000°F 54.3 µohm-in 500°C 137 µohm-cm
1200°F 54.3 µohm-in 600°C 138 µohm-cm
1400°F 53.9 µohm-in 700°C 138 µohm-cm
1600°F 53.5 µohm-in 800°C 137 µohm-cm
1800°F 53.1 µohm-in 900°C 136 µohm-cm
- - 1000°C 135 µohm-cm
Thermal Conductivity RT 68 Btu-in/ft2-hr-°F RT 9.8 W/m-°C
200°F 75 Btu-in/ft2-hr-°F 100°C 10.9 W/m-°C
400°F 87 Btu-in/ft2-hr-°F 200°C 12.5 W/m-°C
600°F 98 Btu-in/ft2-hr-°F 300°C 13.9 W/m-°C
800°F 109 Btu-in/ft2-hr-°F 400°C 15.3 W/m-°C
1000°F 121 Btu-in/ft2-hr-°F 500°C 16.9 W/m-°C
1200°F 132 Btu-in/ft2-hr-°F 600°C 18.3 W/m-°C
1400°F 144 Btu-in/ft2-hr-°F 700°C 19.8 W/m-°C
1600°F 158 Btu-in/ft2-hr-°F 800°C 21.5 W/m-°C
1800°F 175 Btu-in/ft2-hr-°F 900°C 23.4 W/m-°C
- - 1000°C 25.6W/m-°C
Specific Heat RT 0.098 Btu/lb.-°F RT 410 J/Kg-°C
200°F 0.102 Btu/lb.-°F 100°C 428 J/Kg-°C
400°F 0.109 Btu/lb.-°F 200°C 455 J/Kg-°C
600°F 0.115 Btu/lb.-°F 300°C 477 J/Kg-°C
800°F 0.122 Btu/lb.-°F 400°C 503 J/Kg-°C
1000°F 0.128 Btu/lb.-°F 500°C 527 J/Kg-°C
1200°F 0.135 Btu/lb.-°F 600°C 552 J/Kg-°C
1400°F 0.141 Btu/lb.-°F 700°C 576 J/Kg-°C
1600°F 0.148 Btu/lb.-°F 800°C 600 J/Kg-°C
1800°F 0.154 Btu/lb.-°F 900°C 625 J/Kg-°C
- - 1000°C 648 J/Kg-°C
Mean Coefficient of
Thermal Expansion		 70-200°F 7.1 µin/in-°F 25-100°C 12.8 x 10-6 µm/m- °C
70-400°F 7.3 µin/in-°F 25-200°C 13.1 x 10-6 µm/m- °C
70-600°F 7.5 µin/in-°F 25-300°C 13.4 x 10-6 µm/m- °C
70-800°F 7.7 µin/in-°F 25-400°C 13.8 x 10-6 µm/m- °C
70-1000°F 8.0 µin/in-°F 25-500°C 14.2 x 10-6 µm/m- °C
70-1200°F 8.4 µin/in-°F 25-600°C 14.8 x 10-6 µm/m- °C
70-1400°F 8.7 µin/in-°F 25-700°C 15.4 x 10-6 µm/m- °C
70-1600°F 9.2 µin/in-°F 25-800°C 16.0 x 10-6 µm/m- °C
70-1800°F 9.6 µin/in-°F 25-900°C 16.7 x 10-6 µm/m- °C
- - 25-1000°C 17.4 x 10-6 µm/m- °C
Dynamic Modulus
of Elasticity 		RT 30.2 x 106 psi RT 208 GPa
200°F 29.2 x 106 psi 100°C 201 GPa
400°F 28.8 x 106 psi 200°C 199 GPa
600°F 27.7 x 106 psi 300°C 192 GPa
800°F 26.7 x 106 psi 400°C 186 GPa
1000°F 25.6 x 106 psi 500°C 179 GPa
1200°F 24.3 x 106 psi 600°C 171 GPa
1400°F 22.8 x 106 psi 700°C 163 GPa
1600°F 21.2 x 106 psi 800°C 153 GPa
1800°F 18.7 x 106 psi 900°C 142 GPa
- - 1000°C 126 GPa

RT = Room Temperature