Cold-Rolled Sheet, Solution Treated and Aged
Test Temperature |
0.2% Yield Strength |
Ultimate Tensile Strength |
Elongation |
°F |
°C |
ksi |
MPa |
ksi |
MPa |
% |
RT |
RT |
89.2 |
615 |
151.0 |
1041 |
35.8 |
400* |
204* |
82.3* |
567* |
139.6* |
963* |
40.9* |
800* |
427* |
80.4* |
554* |
126.7* |
874* |
39.6* |
1000 |
537 |
76.4 |
527 |
124.8 |
860 |
42.1 |
1200 |
649 |
75.2 |
518 |
130.7 |
901 |
36.9 |
1400 |
760 |
76.0 |
524 |
100.9 |
696 |
26.6 |
1500* |
816* |
68.2* |
470* |
77.3* |
533* |
35.2* |
1600 |
871 |
43 |
296 |
50.5 |
348 |
58.1 |
1700 |
927 |
17.0 |
117 |
25.0 |
172 |
105.2 |
1800 |
982 |
12.3 |
85 |
17.9 |
123 |
95.1 |
2000 |
1093 |
5.5 |
38 |
9.0 |
62 |
103.6 |
* Limited data
Mill Annealed +1472°F/8h/Air Cool
Cold-Rolled Plate, Solution Treated and Aged
Test Temperature |
0.2% Yield Strength |
Ultimate Tensile Strength |
Elongation |
°F |
°C |
ksi |
MPa |
ksi |
MPa |
% |
RT |
RT |
84.7 |
584 |
147.7 |
1018 |
30.4 |
400* |
204* |
74.5* |
514* |
139.6* |
963* |
34.2* |
800* |
427* |
70.9* |
489* |
126.8* |
874* |
41.2* |
1000 |
537 |
74.3 |
512 |
122.6 |
845 |
42.5 |
1200 |
649 |
71.8 |
495 |
125.8 |
867 |
32.7 |
1400 |
760 |
72.5 |
500 |
101.9 |
703 |
19.9 |
1500* |
816* |
64.1* |
442* |
81.8* |
564* |
22.8* |
1600 |
871 |
45.2 |
312 |
53.2 |
367 |
47.5 |
1800 |
982 |
12.5 |
86 |
18.8 |
130 |
101.6 |
2000 |
1093 |
6 |
41 |
9.1 |
63 |
114.8 |
* Limited data
Mill Annealed +1472°F/8h/Air Cool