Tensile Properties

Cold-Rolled and Solution-annealed Sheet, 0.033 to 0.109 in. (0.8 to 2.8 mm) Thick*

Test
Temperature 		Yield Strength
0.2% Offset 		Ultimate Tensile
Strength 		Elongation
°F °C ksi MPa ksi MPa %
RT RT 59.5 410 118.1 815 47.7
1000 538 34.9 240 93.4 645 54.4
1200 649 32.8 225 85.4 590 52.4
1400 760 32.0 220 68.5 470 49.1
1600 871 28.6 195 47.6 330 52.6
1800 982 15.5 105 28.0 195 63.3
2000 1093 8.0 55 14.8 100 55.4

*Based upon 10 or more Tests per condition
RT= Room Temperature

Elevated temperature tensile tests for sheet were performed with a strain rate that is no longer standard.  These results were from tests with a strain rate of 0.005 in./in./minute through yield and a crosshead speed of 0.5 in./minute for every inch of reduced test section from yield through failure. The current standard is to use a strain rate of 0.005 in./in./minute though yield and a crosshead speed of 0.05 in./minute for every inch of reduced test section from yield through failure.

Comparative Yield Strengths (Sheet)

556 - Comparative Yield Strengths (Sheet)

Holt-Rolled and Solution-annealed Plate

Test Temperature Ultimate Tensile Strength 0.2% Yield Strength Elongation
°F °C ksi MPa ksi MPa %
RT RT 114.6 790 54.1 373 51.3
1000 538 95.6 659 33.7 232 58.2
1200 649 87.2 601 33.2 229 55.1
1400 760 63.1 435 34.0 234 57.4
1600 871 37.4 258 26.9 185 87.9
1800 982 20.3 140 13.2 91 96.2
2000 1093 11.2 77 6.7 46 90.3

RT= Room Temperature