Form |
Test Temperature |
Thickness |
0.2%Offset
Yield Strength |
Ultimate Tensile
Strength |
Elongation |
°F |
°C |
in |
mm |
ksi |
MPa |
ksi |
MPa |
% |
Sheet |
RT |
RT |
0.078 |
2 |
51.6 |
356 |
114.9 |
792 |
61 |
Sheet |
400 |
204 |
0.078 |
2 |
42.0 |
290 |
100.6 |
694 |
59 |
Sheet |
600 |
316 |
0.078 |
2 |
35.9 |
248 |
98.8 |
681 |
68 |
Sheet |
800 |
427 |
0.078 |
2 |
32.7 |
225 |
94.3 |
650 |
67 |
Sheet |
400 |
204 |
0.094 |
2.4 |
39.9 |
275 |
101.0 |
696 |
58 |
Sheet |
600 |
316 |
0.094 |
2.4 |
33.5 |
231 |
97.6 |
673 |
64 |
Sheet |
800 |
427 |
0.094 |
2.4 |
29.7 |
205 |
93.5 |
645 |
64 |
Sheet1 |
400 |
204 |
0.063-0.187 |
1.6-4.7 |
42.1 |
290 |
100.8 |
695 |
56 |
Sheet2 |
600 |
316 |
0.063-0.187 |
1.6-4.7 |
37.7 |
260 |
97.0 |
669 |
64 |
Sheet2 |
800 |
427 |
0.063-0.187 |
1.6-4.7 |
34.8 |
240 |
95.0 |
655 |
65 |
Sheet2 |
1000 |
538 |
0.063-0.187 |
1.6-4.7 |
33.8 |
233 |
88.9 |
613 |
60 |
Plate3 |
400 |
204 |
0.188-1.0 |
4.8-25.4 |
38.2 |
263 |
98.9 |
682 |
61 |
Plate3 |
600 |
316 |
0.188-1.0 |
4.8-25.4 |
34.1 |
235 |
94.3 |
650 |
66 |
Plate3 |
800 |
427 |
0.188-1.0 |
4.8-25.4 |
32.7 |
225 |
91.5 |
631 |
60 |
Plate3 |
1000 |
538 |
0.188-1.0 |
4.8-25.4 |
32.8 |
226 |
87.2 |
601 |
59 |
Plate |
RT |
RT |
1.0 |
25.4 |
52.9 |
365 |
113.9 |
785 |
59 |
Plate |
600 |
316 |
1.0 |
25.4 |
36.2 |
250 |
96.3 |
664 |
63 |
Plate |
800 |
427 |
1.0 |
25.4 |
30.5 |
210 |
94.8 |
654 |
61 |
1: Average of 25 tests
2: Average of 34-36 tests
3: Average of 9-11 tests
RT= Room Temperature