Form |
Thickness |
Test |
0.2% Offset |
Ultimate Tensile |
Elongation |
in |
mm |
°F |
°C |
ksi |
MPa |
ksi |
MPa |
% |
Sheet |
0.125 |
3.2 |
RT |
RT |
61 |
421 |
125 |
862 |
53 |
Sheet |
0.125 |
3.2 |
200 |
93 |
55 |
379 |
121 |
834 |
57 |
Sheet |
0.125 |
3.2 |
400 |
204 |
47 |
324 |
110 |
758 |
60 |
Sheet |
0.125 |
3.2 |
600 |
316 |
44 |
303 |
104 |
717 |
63 |
Sheet |
0.125 |
3.2 |
800 |
427 |
42 |
290 |
102 |
703 |
62 |
Sheet |
0.125 |
3.2 |
1000 |
538 |
39 |
269 |
98 |
676 |
59 |
Sheet |
0.125 |
3.2 |
1200 |
649 |
46 |
317 |
104 |
717 |
56 |
Plate |
Multiple* |
RT |
RT |
58 |
400 |
128 |
883 |
58 |
Plate |
Multiple* |
200 |
93 |
54 |
372 |
122 |
841 |
58 |
Plate |
Multiple* |
400 |
204 |
48 |
331 |
115 |
793 |
61 |
Plate |
Multiple* |
600 |
316 |
44 |
303 |
111 |
765 |
62 |
Plate |
Multiple* |
800 |
427 |
41 |
283 |
108 |
745 |
62 |
Plate |
Multiple* |
1000 |
538 |
40 |
276 |
106 |
731 |
62 |
Plate |
Multiple* |
1200 |
649 |
42 |
290 |
107 |
738 |
65 |
*Average values from the testing of 6 lots of plate (of different thicknesses) from three heats.
RT= Room Temperature