Cold-Rolled and 1925°F (1052°C) Mill-Annealed, Sheet
Test Temperature |
0.2% Yield Strength |
Ultimate Tensile Strength |
Elongation |
°F |
°C |
ksi |
MPa |
ksi |
MPa |
% |
RT |
RT |
71.2 |
491 |
133.9 |
923 |
47.5 |
1000 |
538 |
56.3 |
388 |
118.4 |
816 |
54.2 |
1200 |
649 |
55.1 |
380 |
117.7 |
811 |
109.3 |
1400 |
760 |
53.8 |
371 |
71.0 |
490 |
135.0 |
1600 |
871 |
29.6 |
204 |
34.7 |
239 |
160.6 |
1800 |
982 |
9.9 |
68 |
15.3 |
106 |
154.5 |
2000 |
1093 |
5.0 |
35 |
8.7 |
60 |
128.3 |
Hot-Rolled and 1925°F (1052°C) Mill-Annealed, Plate
Test Temperature |
0.2% Yield Strength |
Ultimate Tensile Strength |
Elongation |
°F |
°C |
ksi |
MPa |
ksi |
MPa |
% |
RT |
RT |
60.5 |
417 |
129.6 |
894 |
48 |
800* |
427* |
46.4 |
320 |
116.1 |
800 |
51.5 |
1000 |
538 |
44.8 |
309 |
112.3 |
774 |
52.1 |
1200 |
649 |
43.7 |
301 |
112.7 |
777 |
80.3 |
1400 |
760 |
43.7 |
301 |
71.1 |
490 |
102.2 |
1600 |
871 |
30.6 |
211 |
38.0 |
262 |
115.7 |
1800 |
982 |
11.8 |
81 |
17.3 |
119 |
120.7 |
2000 |
1093 |
5.4 |
37 |
9.3 |
64 |
135.1 |
*Average of results for only two products
RT=Room Temperature
Comparative Elevated Temperature Yield Strengths, Sheet