Tensile Properties

Cold-Rolled and 2250°F (1232°C) Solution-annealed (Sheet)

Test
Temperature
Yield Strength
0.2% Offset
Ultimate Tensile
Strength
Elongation
°F °C ksi MPa ksi MPa %
RT RT 61.3 422 121.6 838 47.2
1000 538 44.0 303 101.5 699 53.7
1200 649 43.6 300 97.2 668 56.7
1400 760 46.9 323 78.3 539 61.2
1600 871 33.9 234 44.7 308 75.0
1800 982 18.2 125 25.0 172 50.2
2000 1093 10.0 69 13.1 90 37.0

Hot-Rolled and 2250°F (1232°C) Solution-annealed (Plate)

Test
Temperature
Yield Strength
0.2% Offset
Ultimate Tensile
Strength
Elongation
°F °C ksi MPa ksi MPa %
RT RT 54.4 375 121.8 840 47.7
1000 538 36.4 251 100.1 690 54.6
1200 649 37.0 255 96.0 662 54.5
1400 760 36.7 253 76.9 530 69.5
1600 871 35.1 242 45.6 315 99.5
1800 982 17.0 118 24.7 171 96.3
2000 1093 9.1 63 13.2 91 92.1

Vacuum Investment Castings (As Cast)

Test
Temperature
Yield Strength
0.2% Offset
Ultimate Tensile
Strength
Elongation Reduction of Area
°F °C ksi MPa ksi MPa % %
RT RT 46.8 325 89.0 615 37.8 37.7
1000 538 33.1 230 65.6 450 38.2 35.9
1200 649 32.4 225 69.8 480 44.2 34.9
1400 760 32.9 225 55.8 385 32.3 36.0
1600 871 26.6 185 41.0 285 19.0 29.8
1800 982 24.8 170 29.4 205 25.5 39.9
2000 1093 12.6 87 12.9 89 41.0 46.6

RT= Room Temperature